Corrosion inhibiting composition and use thereof

ABSTRACT

A CORROSION INHIBITING COMPOSITION OF (1) A DICARBOXYLIC ACID AND (2) POLYMERIC REACTION PRODUCT OF AN EPIHALOHYDRIN COMPOUND AND ALIPHATIC AMINE. THE COMPOSITION IS INCORPORATED IN ANY SUBSTRATE WHICH CONTACTS METAL AND SERVES TO INHIBIT CORROSION OF THE METAL.

United States Patent O 3,705,109 CORROSION INHIBITIN G COMPOSITION AND USE THEREOF Rudolf H. Hausler, Arlington Heights, and Leonard A. Goeller, Des Plaines, Ill., assignors to Universal Oil Products Company, Des Plaines, Ill. No Drawing. Filed Apr. 6, 1970, Ser. No. 26,084 Int. Cl. C23f 11/00 U.S. Cl. 252-392 Claims ABSTRACT OF THE DISCLOSURE A corrosion inhibiting composition of (1) a dicarboxylic acid and (2) polymeric reaction product of an epihalohydrin compound and aliphatic amine. The composition is incorporated in any substrate which contacts metal and serves to inhibit corrosion of the metal.

BACKGROUND OF THE INVENTION In the manufacture, handling, transportation and/ or use of various organic substances, corrosion problems occur due to the presence of corrosive materials, including one or more of oxygen, hydrogen sulfide, carbon dioxide, 2 to 4 carbon atom carboxylic acids, hydrogen halide, halogen salts as sodium chloride, ammonium chloride, etc. or mixtures thereof, as well as the presence of water in solution or in suspension in the organic substances. Illustrative organic substances include particularly hydrocarbon distillates as gasoline, jet fuel, kerosene, lubricating oil, fuel oil, diesel oil, crude oil, etc. Other specific oils include cutting oils, soluble oils, slushing oils, rolling oils, etc. which may be of mineral, animal or vegetable origin. Other organic substances include various coating compositions as grease, wax, household oil, paints, lacquer, etc. Still other organic substances include alcohols, ketones, esters, ethers, dioxane, amino compounds, amides, etc. In spite of all reasonable and practical precautions which are taken to avoid the presence of water, an appreciable quantity of water separation is found as a film or in minute droplets in the pipe line or on container walls or even in small pools at the bottom of the container. This results in corrosion of the metal surfaces and contamination of the organic substance by the corrosion products. In addition to the corrosion described above, corrosion also is encountered in various types of oil wells, including drilling equipment, auxiliary field equipment such as flow lines, separators, tanks, etc., as well as ballast tanks on submersible drilling barges, marine vessels, etc. Corrosion also is encountered in processing equipment including piping, reactors, pumps, heat exchangers, storage tanks, etc.

A myriad of corrosion inhibitors has been proposed heretofore. One class includes various acids, amines, various reaction products of amines, including salts of amines and carboxylic acids, reaction products of amines with epihalohydrin compounds, etc. While many of the prior art inhibitors are very efiective for the purpose, there still is a need to even further improve the effectiveness and also the desire to accomplish satisfactory corrosion inhibition with lower amounts of the inhibitor and thus eifect economy in this art.

DESCRIPTION OF THE INVENTION It now has been found that the corrosion inhibiting properties may be enhanced by utilizing a particular mixture of certain additives. As will be demonstrated in the appended examples, improved corrosion inhibition is obtained with lower amounts of the mixture. Accordingly the desired inhibition is accomplished at a considerable savings in cost.

Patented Dec. 5, 1972 The improved corrosion inhibition is obtained through a mutually related and interdependent coaction between the two components of the mixture. The exact mechanism for these improved results is not fully understood but, after discovery of these improved results, the theory may be advanced that, while one of the components of the mixture possesses corrosion inhibition activity, it also possesses greater dispersant and solvency properties. Accordingly, it may be reasoned that the last named component, while contributing to the corrosion inhibition, also serves to extract the other component, which may possess greater inhibiting potency, from the hydrocarbon phase and to carry the other component into contact with the metal surfaces, at which point both components mutually serve to protect the metal surfaces from corrosion. Regardless of the reasons therefor, the mixture of the present invention does result in improved corrosion inhibition and applicants do not wish to be limited to the explanation offered above.

Certain acids do serve to inhibit rusting of metals in an aerobic environment. However, in an anaerobic environment, the acids are of low effectiveness as corrosion inhibitors. However, the inhibitor composition of the present invention is an effective corrosion inhibitor both in anaerobic and aerobic environments and, as hereinbefore set forth, effects the corrosion inhibition at low concentrations of additive. Thus, the inhibitor composi tion of the present invention offers the dual advantage of also being effective under anaerobic conditions and to accomplish the desired inhibition with low concentrations of additive.

In one embodiment the present invention relates to a corrosion inhibiting composition of (1) from about 50% to about 98% by weight of a 10-50 carbon atom dicarboxylic acid and (2) from about 2% to about 50% by weight of a polymeric reaction product of an epihalohydrin and a 10-30 carbon atom aliphatic amine.

As hereinbefore set forth, one component of the composition is a dicarboxylic acid. Any suitable dicarboxylic acid may be used and contains from 10 to 50 and preferably from 20 to 40 carbon atoms per molecule. A number of dicarboxylic acids are available commercially, generally as a mixed by-product and accordingly marketed at a lower cost. One such dicarboxylic acid is marketed under the trade name of VR-l Acid. This acid is a mixture of polybasic acids, predominantly dicarboxylic acids, and has an average molecular weight of about 750. Another mixed by-product acid is marketed commercially under the trade name of Dimer Acid. Still another such acid is marketed under the trade name of D-SO-MEX acid.

Still another mixed byproduct acid is marketed commercially under the trade name of Empol 222. This dimer acid is a dilinoleic acid and is represented by the following general formula:

This acid is a viscous liquid, having an apparent molecular weight of approximately 600. It has an acid value of 180- 192, an iodine value of -95, a saponification value of 185-195, a neutralization equivalent of 290-310, a refractive index at 25 C. of 1.4919, a specific gravity at 15.5 C./l5.5 C. of 0.95, a flash point of 530 F., a fire point of 600 F and a viscosity at C. of 100 centistokes.

Other dicarboxylic acids include alkyl dicarboxylic acid in which the alkyl contains at least 10 carbon atoms per molecule and thus may comprise alkyl malonic acid, alkyl succinic acid, alkyl glutaric acid, alkyl adipic acid, alkyl pimelic acid, alkyl suberic acid, alkyl azelaic acid, alkyl sebacic acid, alkyl phthalic acid, and higher molecular weight dicarboxylic acids. It is understood that a'mixture' of acids may be employed.

The acid may be formed as a solution in a suitable solvent for ease in handling and using. Any suitable solvent may be used and preferably comprises an aromatic hydrocarbon, including benzene, toluene, xylene, ethylbenzene, diethyl benzene, cumene, etc. or a paraffinic hydrocarbon including hexane, heptane, octane, nonane, decane, undecane, dodecane, etc. but preferably comprises a mixture such as naphtha, kerosene, fuel oil, etc. or an aromatic mixture as, for example, an aromatic residue product. These mixed products generally are available at lower cost and appear to satisfactorily serve as solvent.

As hereinbefore set forth, another component of the inhibitor composition of the present invention is a polymeric reaction product of an epihalohydrin compound and an aliphatic amine. Any suitable aliphatic amine may be used. The amine maybe a primary aliphatic amine and thus will be selected from decyl amine, undecyl amine, dodecyl amine, tridecyl amine, tetradecyl amine, pentadecyl amine, hexadecyl amine, heptadecyl amine, octadecyl amine, nonadecyl amine, eicosyl amine, heneicosyl amine, docosyl amine, tricosyl amine, tetracosyl amine, pentacosyl amine, hexacosyl amine, heptacosyl amine, octacosyl amine, nonacosyl amine and triacontyl amine, as Well as the corresponding alkenyl amines. Conveniently these long chain amines are derived from fatty acids, the amines being referred to herein as fatty amines, and thus include lauryl amine, myristyl amine, palmityl amine, stearyl amine, arachidyl amine, palmitolyl amine, oleyl amine, ricinoleyl amine, linolelyl amine, linolenyl amine, etc.

Mixtures of fatty amines are available commercially under various trade names including Alamine H26D and Armeen HTD. These products comprises mixtures predominating in alkyl amines containing 16 to 18 carbon atoms per alkyl group, although they contain a small amount of alkyl groups having 14 carbon atoms. Other mixed fatty amines include tallow amine, coco amine, palm amine, etc., as well as hydrogenated products thereof.

In another embodiment the amine is an N-aliphaticdiaminoalkane having an aliphatic group of at least 8 and preferably of at least 10 carbon atoms. A particularly preferred N-alkyl-diaminoalkane is an N-alkyl-1,3-diaminopropane including, for example,

N-decyl-l,3-diaminopropane, N-undecyl-1,3-diaminopropane,

N-dodecyl- 1,3-diaminopropane,

N-tridecy l- 1 ,3-diamin0 propane,

N-tetradecyl- 1 3 -diaminopropane, N-pentadecyl-1,3-diaminopropane, N-hexadecyl-l,3-diarninopropane,

N-heptade cyll ,3-diaminoprop ane,

N-octadecyl- 1 ,3 -diaminoprop ane,

N-nonaclecyl- 1 ,S-diaminopropane,

N-eicosyl- 1 ,3 -diaminopropane,

N-heneicosyl- 1 ,3 -diaminopropane, N-docosyl-1,3-diaminopropane,

N-tricosyl- 1 ,3 -diaminopropane, N-tetracosyl-1,3-diaminopropane, N-pentacosyl-l,3-diaminopropane,

N-hexacosyll ,3 -diaminopropane and N-heptacosyl-1,3-diaminopropane.

Here again the aliphatic group conveniently is derived from fatty acids and thus the aliphatic group includes lauryl, myristyl, palmityl, stearyl, arachidyl, palmitolyl, oleyl, ricinoleyl, linoleyl, linolenyl, etc. A number of N- alkyl-1,3-dia-minopropanes are avaliable commerc1ally as mixtures and generally at a lower cost. One such mixture is available commercially under the trade name of Duomeen T in which the alkyl substituents contain from about 12 to about carbon atoms per group and mostly 16 to 18 carbon atoms. Another mixture is available as Diam 26.

Still another commercially available mixture is Duomeen O and comprises N-oleyl-1,3-diaminopropane. Another N-aliphatic-1,3-diaminopropane is Doumeen LPS in which the aliphatic group is derived from phenyl stearic acid. This is a mixed acid in which the phenyl group is positioned on either the 9 or 10 carbon atom of the stearyl chain.

A preferred epihalohydrin compound is epichlorohydrin. Other epichlorohydrin compounds include 1,2-epi-4 chloro-butane, 2,3-epi-4-chlorobutane, 1,2-epi-5-chloropentane, 2,3-epi-5-chloropentane, etc. While the chloro derivatives are preferred, it is understood that the corre sponding bromo and iodo compounds may be employed. 'In some cases epidihalohydrin compounds may be used. It is understood that the different epihalohydrin compounds are not necessarily equivalentand that, as hereinbefore set forth, epichlorohydrin is preferred.

The reaction of amine and epichlorohydrin is effected in any suitable manner. Preferably the reactants are prepared as solutions in suitable solvents, including the solvents hereinbefore set forth and also including alcohol such as ethanol, propanol, butauol, 'etc. Conveniently the reaction is effected by heating the epichlorohydrin solution at reflux conditions with stirring, gradually adding the amine thereto and continuing the heating, preferably at a higher temperature, until the reaction is completed, or the reverse order of adding the reactants may be used. In general, the temperature will range from about 65 to about 215 F. and preferably from about F. to about 215 F. The time of reaction will be sufiicient to effect polymer formation and generally will range from about 2 and preferably from about 4 to 24 hours or more. The organic halide salt, which is formed initially, is converted to an inorganic halide salt, thereby liberating the free amine for further reaction to form the polymeric product. This may be effected in any suitable manner and may be accomplished by reacting the primary reaction product with a strong inorganic base, such as sodium hydroxide, potassium hydroxide, etc., to form the corresponding metal halide. The reaction to form the metal halide is effected at a temperature within the range of from about to about 215 F. and preferably from about to about F. The inorganic base is added in at least two steps with intervening heating and reacting in order to insure liberation of the free amine.

Also it generally is preferred to further heat and react the mixture at a temperature of from about 165 to about 195 F. to insure formation of the desired polymer. The polymeric reaction product may contain from 2 to 20 or more and preferably 3 to 10 recurring units. After formation of the desired polymeric reaction product or prior thereto if desired, the inorganic halide salt is removed in any suitable manner including filtering, centrifugal separation, etc. In some cases it may be of advantage to effect the filtering at an elevated temperature which may be within the range of from about 95 to about 160 F. Detailed information on the preparation of some of these reaction products is contained in US. Pat. 3,189,652 and such details are incorporated by reference into the present specifications.

The polymeric reaction product may be utilized as such for blending with the salt or may be formed as a solution in a suitable solvent. The solvent preferably will be selected from those hereinbefore set forth.

The acid and the polymeric reaction product are commingled in a proportion of from about 50% to about 98% by weight of the acid and from 2% to about 50% by weight of the polymeric reaction product. In a particularly preferred embodiment the acid is in a proportion of from about 90% to about 98% by weight and the polymeric reaction product is in a concentration of about 2% to about 10% by weight. The weight percents used in the present specifications and claims are on the basis of active ingredients and do not include solvent or other components incorporated in the inhibitor compositions.

While the acid and the polymeric reaction product may be added separately in the prescribed proportions to the organic substrate, it is preferred to form a blend of the acid and the polymeric reaction product and to incorporate the blend into the organic substrate. When desired, the inhibitor composition may also contain one or more other ingredients as, for example, a metal deactivator, such as disalicylal diaminopropane, ethylenediamine tetraacetic acid, etc., antioxidants which generally are of the phenolic or amine type, or other additives which normally are incorporated in the substrate. For ease in handling, the final inhibitor composition may be prepared as a solution in a suitable solvent, the solvent preferably being selected from those hereinbefore set forth, and conveniently comprises all or a part of the solvent or solvents originally contained in the acid, polymeric reaction product and other components in the final composition.

It is an important advantage of the present invention that the inhibitor composition is utilized in a comparatively low concentration. The concentration, based on active ingredients, may be within the range of from 1 to 50 p.p.m. (parts per million) of the substrate, although higher concentrations up to 1000 p.p.m. may be employed in special situations encountering excessive corrosion.

As hereinbefore set forth the inhibitor composition of the present invention is used in any substrate which contacts metal and corrosion of the metal is encountered. In one embodiment the inhibitor composition is incorporated in a hydrocarbon substrate and will be added to the substrate in the desired concentration, preferably accompanied by some form of mixing in order to obtain uniform distribution of the inhibitor composition, such as for example by the use of a mixing device, pumping of the mixture, recirculation out of and back into a vessel, or in any other suitable manner.

The following examples are introduced to illustrate further the novelty and utility of the present invention but not with the intention of unduly limiting the same.

EXAMPLE I The polymeric reaction product of this example was prepared by reacting Duomeen T with epichlorohydrin. The reactants were used in substantially equal mole proportions. A solution of epichlorohydrin in alcohol and xylene was charged to a reaction zone and then the desired amount of amine was added in two separate steps. The mixture was stirred and heated to a temperature of 160- 190 F. Subsequently, sodium hydroxide was added in two steps to the reaction mixture, with intervening heating and mixing. After completion of the polymerization, the sodium chloride formed in the reaction was removed by filtering and the alcohol solvent was removed by distillation. The product then is formed as a 50% solution in a xylene solvent.

EXAMPLE II The polymeric reaction product of this example is prepared in substantially the same manner as described in Example I except that the amine used is hydrogenated tallow amine. It will be noted that the aminepsed in Example I is a diaminoalkane, whereas the amine used in this example is a monoamine. Following completion of the reaction, the polymeric reaction product is prepared as a 50% solution in a heavy xylene solvent.

EXAMPLE III Another polymeric reaction is prepared in substantially the same manner as described in Example II except that the amine used in this example is oleyl amine. The polymeric reaction product is prepared as a 50% solution In an aromatic solvent.

EXAMPLE IV A corrosion inhibiting composition is prepared to comprise 70% by weight of D-SO-MEX Acid and 30% by weight of the polymeric reaction product prepared as described in Example I. As hereinbefore set forth, D 50- MEX Acid is a mixed byproduct acid, predominantly dicarboxylic acid, as is available commercially at a lower cost. The acid is prepared as a 50% solution in a heavy xylene solvent for ease of handling. As hereinbefore set forth, the proportions mentioned above are on the basis of active ingredients and are exclusive of solvents.

EXAMPLE V Another corrosion inhibitor composition is prepared to comprise by weight of VR-l Acid and 10% by weight of the polymeric reaction product prepared as described in Example II.

EXAMPLE VI Another corrosion inhibitor composition is prepared to comprise 50% by weight of Empol 222 Acid and 50% by weight of the polymeric reaction product prepared as described in Example III. As hereinbefore set forth this acid is dilinoleic acid.

EXAMPLE VII The corrosion inhibition properties of the mixture of the present invention were determined in a corrosion testing apparatus developed by one of the present applicants and is the subject of a separate application in his name. No novelty is claimed in the present application for the method and apparatus used in these determinations. In general, the method entails preparing a mixture of toluene and water containing 0.0056 N ammonium chloride solution. This mixture, together with 1 atmosphere of hydrogen sulfide, is recirculated over 2 mil thick steel probes. The apparatus provides for measuring the electrical current flowing through the probe during the test. While maintaining a constant electrical potential, the current measurement is recorded graphically. The decrease in current is directly proportional to the increase in total corrosion. Accordingly, by determining the rate of change in current, the corrosion rate, expressed as m.p.y. (mils per year), is determined.

The base current rate (no inhibitor added) averaged approximately 200 m.p.y. When evaluated in the above manner, the inhibitor composition of Example IV, in a total concentration of 1.5 p.p.m., reduced to corrosion rate from about 200 down to about 1 m.p.y., thus showing approximately protection. It will be seen that the use of only 1.5 p.p.m. of the inhibitor composition served to accomplish substantially complete protection.

EXAMPLE VIII The inhibitor composition prepared as described in Example V is incorporated in fuel oil being transported via pipe line and serves to retard corrosion of the piping and pumping equipment.

EXAMPLE IX The corrosion inhibitor composition prepared as described in Example V1 is incorporated into a kerosene stream being pumped into a storage tank and serves to inhibit corrosion of the piping and tank equipment.

EXAMPLE X The corrosion inhibitor composition prepared as described in Example IV is introduced into the overhead line of a crude column and serves to inhibit corrosion of the piping and subsequent heat exchangers, coolers and receivers.

EXAMPLE XI The corrosion inhibitor composition prepared as described in Example IV is incorporated into gasoline and serves to inhibit corrosion of the metal parts contacted by the gasoline.

We claim as our invention:

1. A corrosion inhibiting composition, elfective under aerobic and anaerobic conditions for inhibiting corrosion of metallic surfaces which contact a substrate containing corrosive materials, of (1) from about 50% to about 98% by weight of a 10-50 carbon atom dicarboxylic acid and (2) from about 2% to about 50% by Weight of a polymeric reaction product obtained by reacting from 1 to 1.5 mole proportions of epihalohydrin selected from the group consisting of epichloro-hydrin, 1,2-epi-4-chlorobutane, 2,3-epi-4-chlorobutane, 1,2-epi-5-chloropentane and 2,3-epi-5-chloropentane and corresponding bromo and iodo compounds and from 1 to 2 mole proportions of aliphatic monoor diamine consisting of carbon, hydrogen and amino nitrogen and containing -30 carbon atoms, said polymeric compound containing 2 to 20 recurring units.

2. The composition of claim 1 in which the acid is in a concentration of from about 90% to about 98% by weight and the polymeric reaction product is in a concentration of about 2% to about 10% by weight.

3. The composition of claim 1 in which said dicarboxylic acid is a mixed acid containing from about 20 to about 40 carbon atoms per molecule.

4. The composition of claim 1 in which said aliphatic amine is a mixture of fatty amines predominating in aliphatic groups of from 12 to 20 carbon atoms per molecule.

5. The composition of claim 1 in which said aliphatic amine is hydrogenated tallow amine.

6. The composition of claim 1 in which said aliphatic amine is N-tallow-l,3-diaminopropane.

7. The composition of claim 1 in which said epihalohydrin compound is epichlorohydrin.

8. A method of inhibiting corrosion of metallic surfaces which contact a substrate containing corrosive materials, which comprises incorporating in said substrate a corrosion inhibiting concentration of the composition of claim 1.

9. The substrate of claim 8 being hydrocarbon distillate.

10. The substrate of claim 8 being an overhead stream in a hydrocarbon refining process.

References Cited UNITED STATES PATENTS 3,493,504 2/1970 Buckley 282396 3,017,354 1/1962 Riggs 282396 2,929,696 3/1960 Barusch 282396 X 3,063,790 11/1962 Pollitzer 2l-2 7 3,189,652 6/ 1965 Pollitzer 4472 MAYER WEINBLATT, Primary Examiner US. Cl. X.R.

2l-2.5, 2.7; 4472; 252-855 E, 51.5 A, 148, 396 